Please use this identifier to cite or link to this item:
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/31116| Title: | Efeito combinado da radiação gama e stress cracking no policarbonato. |
| Other Titles: | The combined effect of gamma radiation and stress cracking in polycarbonate. |
| ???metadata.dc.creator???: | MELO, Raphaela Nunes de. RABELLO, Marcelo Silveira. |
| Keywords: | Policarbonato;Stress cracking;Análise fratográfica;Análise calorimétrica;Radiação gama - policarbonato;Ensaio de resistência ao stress cracking;Polycarbonate;Stress cracking;Fratographic analysis;Calorimetric analysis;Gamma radiation - polycarbonate;Stress cracking resistance test |
| Issue Date: | 2009 |
| Publisher: | Universidade Federal de Campina Grande |
| Citation: | MELO, Raphaela Nunes de; RABELLO, Marcelo Silveira. Efeito combinado da radiação gama e stress cracking no policarbonato. In: CONGRESSO DE INICIAÇÃO CIENTÍFICA DA UFCG, 6., 2009, Campina Grande. Anais [...]. Campina Grande - PB, 2009. ISSN: 2177-112X. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/31116 |
| ???metadata.dc.description.resumo???: | Foi estudado o efeito combinado da radiação gama e stress cracking no policarbonato (PC). As amostras de policarbonato foram moldadas por injeção e expostas a diferentes doses de radiação gama. Posteriormente, foram submetidas ao contato com o iso-propanol, utilizado como agente de stress cracking do PC, para que então fosse analisado o comportamento das diferentes amostras. O material foi submetido a ensaios mecânicos de tração, análise do peso molecular viscosimétrico, espectroscopia na região do infravermelho, análise fratográfica (exame visual e microscopia eletrônica de varredura) e análise colorimétrica. Os resultados mostraram que a irradiação prévia do PC intensificou o efeito do stress cracking, o que ficou evidenciado através da diminuição da resistência tênsil e dos danos estéticos causados nas amostras. |
| Abstract: | In this work the combined effect of gamma irradiation and stress cracking was studied in polycarbonate (PC). Tensile test bars were produced by injection moulding and then exposed to different doses of gamma radiation. After that they were submitted to the contact with isopropanol, the stress cracking agent used in this work. The specimens were tested for mechanical properties, viscosity molecular weight, infrared spectroscopy and fractography. The results indicated that the previous radiation intensified the stress cracking effects, as evidenced by the reduction in tensile properties and surface damage caused to the samples. |
| Keywords: | Policarbonato Stress cracking Análise fratográfica Análise calorimétrica Radiação gama - policarbonato Ensaio de resistência ao stress cracking Polycarbonate Stress cracking Fratographic analysis Calorimetric analysis Gamma radiation - polycarbonate Stress cracking resistance test |
| ???metadata.dc.subject.cnpq???: | Engenharia de Materiais. |
| URI: | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/31116 |
| Appears in Collections: | VI CIC. UFCG - Artigos - Engenharias e Ciências Exatas |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| EFEITO COMBINADO DA RADIÇÃO GAMA E STRESS - ANAIS CIC-UFCG 2009..pdf | Efeito combinado da radiação gama e stress cracking no policarbonato. - Anais CIC UFCG 2009 | 870.68 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.